Comparison of tensile properties and work hardening rate of fine and coarse-grained 304 austenitic stainless steel

Document Type : Research Paper

Authors
Saeedeh Afshar 1
Hossein Arabi 2
Bagher Mohammad Sadeghi 3
Mohsen Karimi 4
1 MSc. Student, School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Tehran, Iran.
2 Professor, School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Tehran, Iran.
3 Assistant Professor, School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Tehran, Iran.
4 Assistant Professor, School of Chemical and Materials Engineering, Shahrood University of Technology, Shahrood, Iran.
10.22076/me.2023.533113.1356
Abstract
In this study, the effects of grain size on the tensile properties and the work-hardening behavior of 304 austenitic stainless steel was investigated. For this purpose, the thermomechanical processing was carried out by applying a 75% thickness reduction to the as-received 304 stainless steel sheet followed by annealing at two different temperatures of 750 and 1000 °C to produce sheets with two different fine- and coarse-grained microstructures. The average grain size decreased from 25 μm in the as-received matrix to 1.93 μm in the sample, which was annealed at 750 °C for 90 min (fine-grained sample). Also, the mean grain size of 35.52 μm (coarse-grained sample) was obtained after annealing at 1000 °C for 90 min. XRD and optical microscopy were used for characterizing the microstructure. The tensile tests were performed in the directions of 0°, 45°, and 90° to the rolling direction of the samples. The yield strength of as-received, fine-grained, and coarse-grained samples were obtained 405, 733, and 305 MPa, respectively. However, the total elongation decreased from 73% in the as-received sample to about 52% in the fine-grained sample. The work hardening behavior of both fine- and coarse-grained samples was observed in three stages: an initial sharp drop until a minimum value was reached, then an increase until a maximum value was reached, and finally a reduction in the work hardening rate until the beginning of necking. The work-hardening rate (dσ/dε) of the coarse-grained sample was higher than that of the fine-grained sample. This was due to the higher martensitic transformation rate in the coarse-grained sample.
Keywords
304 austenitic stainless steel
Thermomechanical Processing
Grain Size
Work Hardening
Tensile Properties
[1]        Davis JR. Stainless steels: ASM international; 1994.
[2]        Demeri MY. Advanced high-strength steels: science, technology, and applications: ASM international; 2013.
[3]        Pramanik A, Basak AK. Stainless Steel: Microstructure, Mechanical Properties and Methods of Application: Nova Publisher's; 2015.
 
[4]        AF P, PR R. Decomposition of austenite in austenitic stainless steels. ISIJ international. 2002;42(4):325-7, https://doi.org/10.2355/isijinternational.42.325.
[5]        Eskandari M, Kermanpur A, Najafizadeh A. Formation of nanocrystalline structure in 301 stainless steel produced by martensite treatment. Metallurgical and Materials Transactions A. 2009;40(9):2241-9, https://doi.org/10.1007/s11661-009-9916-z.
[6]        Momeni A, Abbasi S. Repetitive thermomechanical processing towards ultra fine grain structure in 301, 304 and 304L stainless steels. Journal of Materials Science & Technology. 2011;27(4):338-43, https://doi.org/10.1016/S1005-0302(11)60071-6.
[7]        Karimi M, Najafizadeh A, Kermanpur A, Eskandari M. Effect of martensite to austenite reversion on the formation of nano/submicron grained AISI 301 stainless steel. Materials characterization. 2009;60(11):1220-3, https://doi.org/10.1016/j.matchar.2009.04.014.
[8]        Solomon N, Solomon I. Deformation induced martensite in AISI 316 stainless steel. Revista de metalurgia. 2010;46(2):121, http://dx.doi.org/10.3989/revmetalm.0920.
[9]        Das A, Sivaprasad S, Ghosh M, Chakraborti P, Tarafder S. Morphologies and characteristics of deformation induced martensite during tensile deformation of 304 LN stainless steel. Materials Science and Engineering: A. 2008;486(1-2):283-6, https://doi.org/10.1016/j.msea.2007.09.005
[10]      Lichtenfeld JA, Van Tyne CJ, Mataya MC. Effect of strain rate on stress-strain behavior of alloy 309 and 304L austenitic stainless steel. Metallurgical and Materials Transactions A. 2006;37(1):147-61, https://doi.org/10.1007/s11661-006-0160-5.
[11]      Shen Y, Li X, Sun X, Wang Y, Zuo L. Twinning and martensite in a 304 austenitic stainless steel. Materials Science and Engineering: A. 2012;552:514-22. https://doi.org/10.1016/j.msea.2012.05.080.
[12]      Zhao J, Jiang Z. Thermomechanical processing of advanced high strength steels. Progress in Materials Science. 2018;94:174-242, https://doi.org/10.1016/j.pmatsci.2018.01.006.
[13]      Sohrabi MJ, Naghizadeh M, Mirzadeh H. Deformation-induced martensite in austenitic stainless steels: a review. Archives of Civil and Mechanical Engineering. 2020;20(4):1-24, https://doi.org/10.1007/s43452-020-00130-1.
[14]      Forouzan F, Najafizadeh A, Kermanpur A, Hedayati A, Surkialiabad R. Production of nano/submicron grained AISI 304L stainless steel through the martensite reversion process. Materials Science and Engineering: A. 2010;527(27-28):7334-9, https://doi.org/10.1016/j.msea.2010.08.002.
[15]      Kumar BR, Sharma S, Mahato B. Formation of ultrafine grained microstructure in the austenitic stainless steel and its impact on tensile properties. Materials Science and Engineering: A. 2011;528(6):2209-16, https://doi.org/10.1016/j.msea.2010.11.034.
[16]      Talonen J, Hänninen H, Nenonen P, Pape G. Effect of strain rate on the strain-induced γ→ α′-martensite transformation and mechanical properties of austenitic stainless steels. Metallurgical and materials transactions A. 2005;36(2):421-32, https://doi.org/10.1007/s11661-005-0313-y.
[17]      Tsuchida N, Morimoto Y, Tonan T, Shibata Y, Fukaura K, Ueji R. Stress-induced martensitic transformation behaviors at various temperatures and their TRIP effects in SUS304 metastable austenitic stainless steel. ISIJ international. 2011;51(1):124-9, https://doi.org/10.2355/isijinternational.51.124.
[18]      De AK, Speer JG, Matlock DK, Murdock DC, Mataya MC, Comstock RJ. Deformation-induced phase transformation and strain hardening in type 304 austenitic stainless steel. Metallurgical and Materials Transactions A. 2006;37(6):1875-86, https://doi.org/10.1007/s11661-006-0130-y.
[19]      Soares GC, Rodrigues MCM, Santos LdA. Influence of temperature on mechanical properties, fracture morphology and strain hardening behavior of a 304 stainless steel. Materials Research. 2017;20:141-51, https://doi.org/10.1590/1980-5373-MR-2016-0932.
[20]      Byun T, Hashimoto N, Farrell K. Temperature dependence of strain hardening and plastic instability behaviors in austenitic stainless steels. Acta Materialia. 2004;52(13):3889-99, https://doi.org/10.1016/j.actamat.2004.05.003.
[21]      Xu D, Wan X, Yu J, Xu G, Li G. Effect of cold deformation on microstructures and mechanical properties of austenitic stainless steel. Metals. 2018;8(7):522, https://doi.org/10.3390/met8070522.
[22]      Xu D, Wan X, Yu J, Xu G, Li G. Effect of grain refinement on strain hardening and fracture in austenitic stainless steel. Materials Science and Technology. 2018;34(11):1344-52, https://doi.org/10.1080/02670836.2018.1451735.
[23]      Naghizadeh M, Mirzadeh H. Effects of grain size on mechanical properties and work‐hardening behavior of AISI 304 austenitic stainless steel. Steel research international. 2019;90(10):1900153, https://doi.org/10.1002/srin.201900153.
[24]      Naghizadeh M, Mirzadeh H. Microstructural evolutions during annealing of plastically deformed AISI 304 austenitic stainless steel: martensite reversion, grain refinement, recrystallization, and grain growth. Metallurgical and Materials Transactions A. 2016;47(8):4210-6, https://doi.org/10.1007/s11661-016-3589-1.
[25]      Moser NH, Gross TS, Korkolis YP. Martensite formation in conventional and isothermal tension of 304 austenitic stainless steel measured by X-ray diffraction. Metallurgical and Materials Transactions A. 2014;45(11):4891-6, https://doi.org/10.1007/s11661-014-2422-y
[26]      Somani M, Juntunen P, Karjalainen L, Misra R, Kyröläinen A. Enhanced mechanical properties through reversion in metastable austenitic stainless steels. Metallurgical and Materials transactions A. 2009;40(3):729-44, https://doi.org/10.1007/s11661-008-9723-y
[27]      Reed-Hill RE, Abbaschian R, Abbaschian R. Physical metallurgy principles: Van Nostrand New York; 1973.
[28]      Furukawa M, Horita Z, Nemoto M, Valiev R, Langdon T. Microhardness measurements and the Hall-Petch relationship in an Al Mg alloy with submicrometer grain size. Acta Materialia. 1996;44(11):4619-29, https://doi.org/10.1016/1359-6454(96)00105-X.
[29]      Mirzadeh H, Najafizadeh A. Correlation between processing parameters and strain-induced martensitic transformation in cold worked AISI 301 stainless steel. Materials characterization. 2008;59(11):1650-4, https://doi.org/10.1016/j.matchar.2008.03.004.
[30]      Lee C-Y, Yoo C-S, Kermanpur A, Lee Y-K. The effects of multi-cyclic thermo-mechanical treatment on the grain refinement and tensile properties of a metastable austenitic steel. Journal of alloys and compounds. 2014;583:357-60, https://doi.org/10.1016/j.jallcom.2013.08.161.
[31]      Varma S, Kalyanam J, Murk L, Srinivas V. Effect of grain size on deformation-induced martensite formation in 304 and 316 stainless steels during room temperature tensile testing. Journal of materials science letters. 1994;13(2):107-11, https://doi.org/10.1007/BF00416816.
[32]      Ulvan E, Koursaris A. The effect of grain size on the bulk formability and tensile properties of austenitic stainless steel types 304 and 316. Metallurgical Transactions A. 1988;19(9):2287-98, https://doi.org/10.1007/BF02645052.
[33]      Meyers MA, Chawla KK. Mechanical behavior of materials: Cambridge university   press; 2008.

  • Receive Date 10 July 2022
  • Revise Date 16 December 2022
  • Accept Date 01 January 2023